产品描述

施工工艺:
Construction technology:
1、系列无机纤维喷涂产品采用成套先进的专业喷涂设备机械化施工
1. A series of inorganic fibre spraying products are mechanized by a set of advanced professional spraying equipment.
2、纤维棉和专用喷涂粘接剂经专用设备高速喷出,在喷头端口充分混合,以一定压力均匀喷涂在基体表面,从而形成密闭无缝的绝热吸声层。其表面平整、纤维分布均匀,无影响使用的分层、孔洞、裂缝等缺陷。
2. Fiber cotton and special spraying adhesives are sprayed out at high speed by special equipment. They are fully mixed at the nozzle ports and sprayed uniformly on the surface of the matrix at a certain pressure, thus forming a sealed seamless adiabatic sound absorption layer. Its surface is smooth and the fibers are evenly distributed. There are no defects such as delamination, holes and cracks that affect the use.
一天喷多少量得看有多少设备,多少人,详细能喷多少可以咨询一下东台市科霍新材料有限公司,专业做无机纤维喷涂施工的,可以为你详细的解答。
The amount of spraying a day depends on how many equipment, how many people, detailed spraying can consult Beijing Haina Lianchang Company, specializing in inorganic fiber spraying construction, can give you a detailed answer.
施工流程:
Construction process:
施工前准备→基面处理→喷涂作业→表面修整→喷涂场地清理→质量验收→喷涂养护
Pre-construction preparation base treatment spraying operation surface finishing spraying site cleaning quality acceptance spraying maintenance
天津矿物纤维吸音喷涂棉厂家
随着节能减排落实为政策指标,大量的节能环保材料应运而生。以防火、保温、吸声降噪三大性能兼具的“矿物纤维喷涂”成为新型节能环保材料的代表,并以其快速、便捷、技术良好等优势,在众多节能环保施工方案中脱颖而出。“矿物纤维喷涂”技术在大量工程建筑中得到应用,如:鸟巢、国家体育馆、首都机场新航站楼、上海世博会企业馆、京沪高铁
上海虹桥枢纽、南京南站枢纽等。随着此项技术的不断发展与改进,矿物纤维喷涂的应用领域不断扩大,已成功的运用在地下车库、设备机房、外墙、交通枢纽、体育场馆、艺术中心、博物馆、厂房等几十类场所中。
工艺特性
矿物纤维喷涂与市场上具有防火、保温、吸声降噪等功能的传统材料相比,具有独特的技术、功能优势。
  1.矿物纤维喷涂具有防火、保温、吸声降噪的三大特性,可同时解决多重问题、减少重复施工。
  2.适合任何建筑形状表面,尤其适合复杂结构和异型结构表面,保持建筑原有构造。
  3.无接缝,具有较好密闭性、可提高综合节能效果。
  4.适合钢材、混凝土、木材、铝塑板等基材表面。
  5.采用专业化喷涂设备,施工便捷、效率高,节省人工及时间。
  6.表面可进行不同的装饰处理,增加其美观性和装饰效果。
工艺流程
矿物纤维喷涂棉和专用喷涂胶粘剂经专用设备高速喷出,在喷头端口充分混合,以一定压力均匀喷涂在基体表面,从而形成密闭无缝的绝热吸声层。其表面平整、纤维分布均匀,无影响使用的分层、孔洞、裂缝等缺陷
天津矿物纤维吸音喷涂棉厂家
施工注意事项
Matters needing attention in construction
对喷涂后的保温吸声层,应提供通风、干燥环境,通常在平均温度25℃,相对湿度≤60%时,依据不同厚度干燥固化时间为24~72小时,此后可进行装饰等其他工序。
For the thermal insulation and sound absorption layer after spraying, ventilation and drying environment should be provided. Usually, when the average temperature is 25 C and the relative humidity is less than 60%, the drying and curing time is 24-72 hours according to different thickness. After that, other processes such as decoration can be carried out.
喷涂成品保护
PROTECTION OF SPRAYING PRODUCTS
喷涂前应安装各种管线、风道等设备吊挂件,避免喷涂完工后在基面钻孔、剔凿。
Before spraying, hangers of various pipelines, air ducts and other equipment should be installed to avoid drilling and chipping on the base after spraying.
喷涂成品在干燥固化期间,避免受到机械碰撞及雨水冲刷。
During the drying and solidification period, the finished product of spraying should be avoided from mechanical collision and rainwater erosion.
对于喷涂层局部因受到碰撞而造成破损时,应进行局部修补;对于经常处于容易受到机械碰撞的部位,可贴覆玻璃纤维布或其它防护材料,用以对纤维层表面进行保护。
Local repairs should be made when the sprayed coating is damaged due to collision. For those parts which are often vulnerable to mechanical collision, glass fiber cloth or other protective materials can be coated to protect the surface of the fiber layer.
保持喷涂区域环境清洁,避免灰尘飞扬,污染成品喷涂层表面。
Keep the spraying area clean, avoid dust flying, and pollute the surface of finished product spraying coating.
喷涂施工过程中,喷涂操作人员应按照国家劳动保护条例相关规定,佩带防尘口罩,高空操作人员应佩带安全带等防护用具。
During spraying construction, spraying operators should wear dust-proof masks and safety belts in accordance with the relevant provisions of the State Labor Protection Regulations.
天津矿物纤维吸音喷涂棉厂家
超细无机纤维和专用喷涂胶粘剂经专用设备高速喷出,在喷头端口充分混合,以一定压力均匀喷涂在基体表面,从而形成密闭无缝的绝热吸声层。其表面平整、纤维分布均匀,无影响使用的分层、孔洞、裂缝等缺陷
好的无机纤维喷涂棉喷涂均匀,省棉,省时,用起来更经济。 产品性能:
1.有机物含量:≤0.5% 2.导热系数:≤0.044W/m.K(测试平均温度70℃+ 70±52℃),测试密度150kg/m3) 3.产品执行标准Q/T0IH 3-20055.